| ▶ 금속 및 관련제품 |
| ASME BPVC.II.A-2025 |
MATERIALS
Part A
Ferrous Material
Specifications
(Beginning to SA-450)
-SA-370 Test Methods and Definitions for Mechanical Testing of Steel Products
- Tension Test
- Bend Test
- Hardness Test
16. Brinell Test
17. Rockwell Test
- Charpy Impact Testing |
- Tension Test : Max. 200 kN
- Bend Test : Max. 490 kN
- Hardness Test
16. Brinell Test : Max. 29 420 N
17. Rockwell Test : Max. 1 471 N
- Charpy Impact Testing : Max. 400 J |
소재지 |
| ASME BPVC.IX-2025 |
QUALIFICATION STANDARD FOR WELDING, BRAZING, AND FUSING PROCEDURES; WELDERS; BRAZERS; AND WELDING, BRAZING, AND FUSING OPERATORS
- QW-150 Tension Tests
- QW-160 Guided-Bend Tests |
- QW-150 Tension Tests : Max. 800 kN(용접부 인장)
- QW-160 Guided-Bend Tests : Max. 490 kN (용접부 굽힘) |
소재지 |
| ASTM A370-24a |
Standard Test Methods and Definitions for Mechanical Testing of Steel Products
- Tension Test
- Bend Test
- Hardness Test
17. Brinell Test
18. Rockwell Test
- Charpy Impact Testing |
- Tension Test:
Max. 200 kN
- Bend Test:
Max. 980 kN
- Hardness Test
17. Brinell Test:
Max. 29 420 N
18. Rockwell Test:
Max. 1 471 N
- Charpy Impact
Testing:Max. 434 J |
소재지 |
| ASTM E 23-25 |
Standard Test Methods for Notched Bar Impact Testing of Metallic Materials |
Max. 434 J |
소재지 |
| ASTM E 407-23 |
Standard practice for microetching metals and alloys |
75 배 ~ 500 배 |
소재지 |
| ASTM E10-23 |
Standard Test Method for Brinell Hardness of Metallic Materials |
Max. 29 420 N |
소재지 |
| ASTM E112-25 |
Standard Test Methods for Determining Average Grain Size
10. Comparison procedure |
75 배 ~ 500 배 |
소재지 |
| ASTM E18-25 |
Standard Test Methods for Rockwell Hardness of Metallic Materials |
Scale B, C, 30N, 30T |
소재지 |
| ASTM E1820-25a |
Standard Test Method for Measurement of fracture Toughness |
Max. 250 kN |
소재지 |
| ASTM E190-21 |
Standard Test Method for Guided Bend Test for Ductility of Welds |
Max. 490 kN |
소재지 |
| ASTM E1921-25 |
Standard Test Method for Determination of reference Temperature, T0. For Ferritic Steels in the Transition Range |
Max. 250 kN |
소재지 |
| ASTM E290-22 |
Standard Test Methods for Bend Testing of Material for Ductility |
Max. 490 kN |
소재지 |
| ASTM E340-23 |
Standard Practice for
Macroetching Metals and Alloys |
0.3 배 ~ 50 배 |
소재지 |
| ASTM E381-22 |
Standard Method of Macroetch Testing Steel Bars, Billets, Blooms, and Forgings |
0.3 배 ~ 50 배 |
소재지 |
| ASTM E45-25 |
Standard Test Methods for Determining the Inclusion Content of Steel
12. Method A(Worst fields)
15. Method D(Low inclusiom content) |
100 배 ~ 500 배 |
소재지 |
| ASTM E8/E8M-25 |
Standard Test Methods for
Tension Testing of Metallic Materials |
Max. 200 kN
Elongation : Max. 100 %
Reduction Area : Max. 100 % |
소재지 |
| BS EN ISO 148-1:2016 |
Metallic materials — Charpy pendulum impact test Part 1: Test method
(ISO 148-1:2016) |
Max. 400 J |
소재지 |
| BS EN ISO 5173:2023 |
Destructive tests on welds in metallic materials -- Bend tests |
Max. 490 kN |
소재지 |
| BS EN ISO 6506-1:2014 |
Metallic materials — Brinell hardness test Part 1: Test method |
Max. 29 420 N |
소재지 |
| BS EN ISO 6508-1:2023 |
Metallic materials — Rockwell hardness test Part 1: Test method (ISO 6508-1:2023) |
Scale B, C, 30N, 30T |
소재지 |
| BS EN ISO 6892-1:2019 |
Metallic materials — Tensile testing
Part 1: Method of test at room temperature |
Max. 200 kN
Elongation : Max. 100 %
Reduction Area : Max. 100 % |
소재지 |
| BS EN ISO 7438:2020 |
Metallic materials -- Bend test |
Max. 490 kN |
소재지 |
| ISO 12135:2021 |
Metallic materials - Unified method of test for the determination of quasistatic fracture toughness |
Max. 250 kN |
소재지 |
| KS B 0802:2003 |
금속 재료 인장 시험 방법
(상․하 항복점, 내력, 인장 강도, 인장하중, 연신율, 단면수축률) |
Max. 200 kN
연신율 : Max. 100 %
단면수축율 : Max. 100 % |
소재지 |
| KS B 0804:2001 |
금속 재료 굽힘 시험 |
Max. 490 kN |
소재지 |
| KS B 0805:2000 |
금속 재료의 브리넬 경도 시험 방법 |
Max. 29 420 N |
소재지 |
| KS B 0806:2000 |
금속재료의 로크웰 경도시험 방법 |
Scale B, C, 30N, 30T |
소재지 |
| KS B 0810:2003 |
금속 재료 충격 시험 방법
(흡수에너지, 파면율, 천이온도, 가로변형량) |
Max. 400 J |
소재지 |
| KS B 0811:2003 |
금속 재료의 비커스 경도 시험 방법 |
Max. 294 N |
소재지 |
| KS B ISO 4136:2012 |
금속 재료 용접부의 파괴 시험 - 횡방향 인장시험 |
Max. 800 kN |
소재지 |
| KS D 0205:2002 |
강의 페라이트 및 오스테나이트 결정 입도 시험법(현미경 관찰법) |
75 배 ~ 500 배 |
소재지 |
| KS D 0210:1992 |
강의 매크로 조직 시험 방법 |
0.3 배 ~ 50 배 |
소재지 |
| ▶ 철강 |
| KS D 1652:2022 |
철 및 강 - 스파크 방전 원자 방출 분광 분석 방법 |
정량범위(%)
탄소(0.01 ~ 2.0)
규소(0.01 ~ 2.5)
망가니즈(0.01 ~ 19.7)
인(0.002 ~ 0.5)
황(0.001 ~ 0.053)
니켈(0.01 ~ 35)
크로뮴(0.01 ~ 25)
몰리브데넘(0.01 ~ 9.0)
구리(0.01 ~ 3.9)
텅스텐(0.01 ~ 20.0)
바나듐(0.01 ~ 5.0)
코발트(0.01 ~ 10.0)
타이타늄(0.005 ~ 2.0)
알루미늄(0.005 ~ 1.0)
비소(0.001 ~ 0.050)
주석(0.006 ~ 0.030)
붕소(0.000 5 ~ 0.020)
납(0.001 ~ 0.050)
지르코늄(0.001 ~ 0.05)
나이오븀(0.001 ~ 0.05)
마그네슘(0.001 ~ 0.05)
칼슘(0.001 ~ 0.01)
탄탈럼(0.02 ~ 0.10)
안티모니(0.008 ~ 0.03) |
소재지 |
| KS D 1778:2023 |
금속 재료의 산소정량 방법 통칙
9.1 비활성 가스 융해-적외선 흡수법 |
정량범위(%)
산소
(0.002 6 ~ 0.036 5) |
소재지 |
| KS D 1779:2016 |
금속 재료의 황 정량 방법 통칙
9.5 적외선 흡수법 |
정량범위(%)
황
(0.001 0 ~ 0.053) |
소재지 |
| KS D 1780:2016 |
금속 재료의 탄소 정량 방법 통칙
9.7 적외선 흡수법 |
정량범위(%)
탄소
(0.008 ~ 3.35) |
소재지 |
| KS D 1811:2003 |
철 및 강의 질소 분석 방법
3.4 비활성 기체 운반 융해-열 전도도법 |
정량범위(%)
질소
(0.004 5 ~ 0.535) |
소재지 |