| ▶ 금속 및 관련제품 |
| AS 1391:2020 |
Metallic materials - Tensile testing - Method of test at room temperature |
1 200 kN 이하 |
소재지 |
| AS 1544.2-2003 |
Method for impact tests on metals part 2: Charpy V-notch |
750 J 이하 |
소재지 |
| BS 7448-1:1991 |
Fracture mechanics toughness tests Part 1: Method for determination of KIc, critical CTOD and critical J values of metallic materials |
피로시험 : 500 kN 이하,
파괴시험 : 2 000 kN 이하 |
소재지 |
| BS 7448-2:1997 |
Fracture mechanics toughness tests Part 2: Method for determination of KIc, critical CTOD and critical J values of welds in metallic materials |
피로시험 : 500 kN 이하,
파괴시험 : 2 000 kN 이하 |
소재지 |
| BS EN ISO 15653:2018 |
Metallic materials - Method of test for the determination of quasistatic fracture toughness of welds |
피로시험 : 500 kN 이하,
파괴시험 : 2 000 kN 이하 |
소재지 |
| ISO 12135:2021 |
Metallic materials - Unified method of test for the determination of quasistatic fracture toughness |
피로시험 : 500 kN 이하,
파괴시험 : 2 000 kN 이하 |
소재지 |
| ISO 148-1:2016 |
Metallic materials - Charpy pendulum impact test - Part 1: Test method |
750 J 이하 |
소재지 |
| ISO 15653:2018 |
Metallic materials – Method of test for the determination of quasistatic fracture toughness of welds |
피로시험 : 500 kN 이하,
파괴시험 : 2 000 kN 이하 |
소재지 |
| ISO 6892-1:2019 |
Metallic materials - Tensile testing - Part 1: Method of test at room temperature |
1 200 kN 이하 |
소재지 |
| JIS Z 2241 : 2022/AMENDMENT 1:2023 |
Metallic materials – Tensile testing – Method of test at room temperature (Amendment 1) |
1 200 kN 이하 |
소재지 |
| JIS Z 2242:2023 |
Method for Charpy pendulum impact test of metallic materials |
750 J 이하 |
소재지 |
| KS B 0802:2003 |
금속 재료 인장 시험 방법
|
1 200 kN 이하 |
소재지 |
| KS B 0810:2003 |
금속 재료 충격 시험 방법 |
750 J 이하 |
소재지 |
| ▶ 철강 |
| AS/NZS 1050.16:1994 |
Methods for the analysis of iron and steel Part 16: Determination of sulfur content - Infrared absorption method after combustion in an induction furnace |
S : (0.002 ~ 0.10) % |
소재지 |
| AS/NZS 1050.32:1994 |
Methods for the analysis of iron and steel Part 32: Determination of carbon content - Infrared method |
C : (0.002 ~ 3.0) % |
소재지 |
| ISO 13902:1997 |
Steel and iron - Determination of high sulfur content - Infrared absorption method after combustion in an induction furnace |
S : (0.10 ~ 0.3) % |
소재지 |
| ISO 15350:2000 |
Steel and iron - Determination of total carbon and sulfur content - Infrared absorption method after combustion in an induction furnace (routine method)
Infrared (IR) absorption for carbon - Method A
Infrared absorption for sulfur - Method A |
C : (0.005 ~ 3.0) %,
S : (0.005 ~ 0.3) % |
소재지 |
| ISO 4935:1989 |
Steel and iron - Determination of sulfur content - Infrared absorption method after combustion in an induction furnace |
S : (0.002 ~ 0.10) % |
소재지 |
| ISO 9556:2025 |
Steel and iron - Determination of total carbon content - Infrared absorption method after combustion in an induction furnace |
C : (0.003 ~ 3) % |
소재지 |
| JIS G 1211-3:2018/AMENDMENT 1:2024 |
Iron and steel - Determination of carbon - Part 3: Infrared absorption method after combustion (Amendment 1) |
C : (0.003 ~ 3) % |
소재지 |
| JIS G 1215-4:2018/AMENDMENT 1:2024 |
Iron and steel - Determination of sulfur - Part 4: Infrared absorption method after combustion in an induction furnace (Amendment 1) |
S : (0.002 ~ 0.10) % |
소재지 |
| JIS G 1253:2002/AMENDMENT 1:2013 |
Iron and steel - Method for spark discharge atomic emission spectrometric analysis (Amendment 1) |
C : (0.002 ~ 3) %,
Si : (0.002 ~ 3) %,
Mn : (0.003 ~ 20) %,
P : (0.000 5 ~ 0.3) %,
S : (0.000 5 ~ 0.1) %,
Ni : (0.002 ~ 10) %,
Cr : (0.002 ~ 18) %,
Mo : (0.001 ~ 2) %,
Cu : (0.001 ~ 2) %,
W : (0.005 ~ 1.4) %,
V : (0.001 ~ 0.8) %,
Co : (0.001 ~ 0.3) %,
Ti : (0.000 5 ~ 0.3) %,
Al : (0.001 ~ 5) %,
As : (0.001 ~ 0.3) %,
Sn : (0.001 ~ 0.1) %,
B : (0.000 1 ~ 0.01) %,
Pb : (0.001 ~ 0.01) %,
Zr : (0.001 ~ 0.1) %,
Nb : (0.001 ~ 0.4) %,
Ca : (0.000 1 ~ 0.003) %,
Sb : (0.008 ~ 0.08) % |
소재지 |
| JIS G 1258-1:2014 |
Iron and steel - ICP atomic emission spectrometric method - Part 1: Determination of various elements - Decomposition with acids and fusion with potassium disulfate |
Si : (0.01 ~ 0.6) %,
Mn : (0.01 ~ 2.0) %,
P : (0.003 ~ 0.10) %,
Ni : (0.01 ~ 4.00) %,
Cr : (0.01 ~ 3.0) %,
Mo : (0.01 ~ 1.2) %,
Cu : (0.01 ~ 0.50) %,
V : (0.002 ~ 0.50) %,
Co : (0.003 ~ 0.20) %,
Ti : (0.001 ~ 0.3) %,
Al : (0.004 ~ 0.10) % |
소재지 |
| KS D 1652:2022 |
철 및 강 - 스파크 방전 원자 방출 분광 분석 방법 |
C : (0.002 ~ 3) %,
Si : (0.002 ~ 3) %,
Mn : (0.003 ~ 20) %,
P : (0.000 5 ~ 0.3) %,
S : (0.000 5 ~ 0.1) %,
Ni : (0.002 ~ 10) %,
Cr : (0.002 ~ 18) %,
Mo : (0.001 ~ 2) %,
Cu : (0.001 ~ 2) %,
W : (0.005 ~ 1.4) %,
V : (0.001 ~ 0.8) %,
Co : (0.001 ~ 0.3) %,
Ti : (0.000 5 ~ 0.3) %,
Al : (0.001 ~ 5) %,
As : (0.001 ~ 0.3) %,
Sn : (0.001 ~ 0.1) %,
B : (0.000 1 ~ 0.01) %,
Pb : (0.001 ~ 0.01) %,
Zr : (0.001 ~ 0.1) %,
Nb : (0.001 ~ 0.4) %,
Ca : (0.000 1 ~ 0.003) %,
Sb : (0.008 ~ 0.08) % |
소재지 |
| KS D 1673-1:2023 |
철 및 강 - 유도결합 플라스마 방출 분광 분석법 - 제1부: 일반사항 |
- |
소재지 |
| KS D 1673-3:2023 |
철 및 강 - 유도결합 플라스마 방출 분광 분석법 - 제3부: 다원소의 정량 - 황산 인산 분해법 |
Mn : (0.01 ~ 1.80) %,
Ni : (0.01 ~ 4.00) %,
Cr : (0.01 ~ 3.00) %,
Mo : (0.01 ~ 1.20) %,
Cu : (0.01 ~ 0.50) %,
V : (0.01 ~ 0.50) %,
Co : (0.01 ~ 0.20) %,
Ti : (0.001 ~ 0.300) % |
소재지 |
| KS D 1673-4:2025 |
철 및 강 - 유도결합 플라스마 원자 방출 분광 분석법 - 제4부: 다원소의 정량 - 산 분해 및 탄산소듐 용융법 |
Si : (0.10 ~ 0.60) %,
Mn : (0.01 ~ 1.80) %,
P : (0.003 ~ 0.090) %,
Ni : (0.02 ~ 4.00) %,
Cr : (0.03 ~ 3.00) %,
Mo : (0.10 ~ 1.20) %,
Cu : (0.01 ~ 0.50) %,
V : (0.01 ~ 0.50) %,
Co : (0.01 ~ 0.20) %,
Ti : (0.001 ~ 0.300) %,
Al : (0.004 ~ 0.100) % |
소재지 |
| KS D ISO 13902:1997 |
강 및 철 중의 고함량의 황 분석 - 유도 로에서 연소 후 적외선 흡수법 |
S : (0.10 ~ 0.3) % |
소재지 |
| KS D ISO 15350:2000 |
철 및 강 - 총 탄소 및 황 분석방법 - 유도로에서 연소후 적외선 흡수법(일반 방법)
탄소에 대한 자외선(IR) 흡수 - 방법A
황에 대한 자외선(IR) 흡수 -방법A |
C : (0.005 ~ 3) %,
S : (0.005 ~ 4.3) % |
소재지 |
| KS D ISO 4935:1989 |
철 및 강 - 총 황 함유량 분석 방법 - 유도로에서 연소 후 적외선 흡수법 |
S : (0.002 ~ 0.10) % |
소재지 |
| KS D ISO 9556:1989 |
철 및 강 - 총 탄소 함유량의 정량 - 유도로 연소 후 적외선 흡수법 |
C : (0.003 ~ 3.0) % |
소재지 |